I'm interested in fine stringer work and find that most bullseye colours lack density when pulled thin, or they sink in and merge. What do others do about this? Are there particular combinations that work? Also I read somewhere that you could pull stringer from enamels- does this get round the problem? & how do you do it - do you melt a bit of glass and roll it in the enamel and pull?
sorry for so many q's, and thanks.