I have some millefiori left over from the microwave kiln firing fad - I think they're coe100 - will they be ok to add to beads do you think?
no harm in trying and should be ok i would have thought ....use the 10% rule and i would not encase just in case
Ok Sarah, thanks - I'll try it, fingers crossed!
I made some coe 100 murrini (P & T) and decided to try them on effetre - it was problematic I have to say. Those that I didn't melt in simply popped off in the kiln. Those I did melt in, only one didn't crack immediately, it waited a day. I think it's because, unlike frit, it's a relatively large bit of glass in one spot, rather than dispersed equally (although I could be wrong and probably am!) Always worth a try though. ;D