Did a silly thing this evening :-[ - I've been trying to make some decent swap beads for Friday's meeting at Di's, so have been shoe-horning in a few extra sessions...well today I just thought I'd squeeze one more bead into the time before I should have been making dinner for the hungry menfolk, then quickly tapped in the up, up, start.........but I miss-tapped and got a different reading to usual and panicked!!! With hindsight all I should have done was wait for the reading to clear and do it again. But, oh no, I got all technical and turned off and started trying to reprogram - took me several minutes to calm down and sort it out and by then it had cooled down to 460 degrees. Don't know if the beads will have survived that.... :-\
I'm sure beads cool way quicker than that in my fibre blanket, I guess if you got it back on again it'll be fine? Fingers crossed :D
I'm sure they'll be fine Marg!
I've pressed the wrong buttons before and I just set the programme running again from scratch and then re-jump the segment pressing the right buttons!
When I first got my kiln, a few weeks ago, I tried to skip to the next segment and got in a heck of a mess. Meanwhile temperature was droipping like a stone. I turned it off then started again and the beads survived. In fact they must be reasonably OK as I managed to drop them all over the garden, falling over one of the cats, when I was bringing them into the house. I trod on a few (I'm under tall for my weight) and they are fine. I guess these things are tougher than we think.
One of my cats has taken to fishing beads out of the plastic tub I put them in, throwing across the conservatory and then playing with them. He quite likes the mucky bead cleaning water as well. I do hate it when I am forced to be tidy by my cat!!
Hi,
Now do a batch anneal and they will be fine, there are programs for this on the forum any problems, pm your phone number and i will talk you through later tonight.
Dianne ;D ;D
Well given that the strain temperature point for soft glass is around 454, and you didn't get that low, I'm sure they'll be fine. :)
I'm sure they'll be fine, if in doubt pop them back in on a batch anneal programme. The biggest boob I ever made was to put the wrong programme on and when I opened the door the next morning they were all welded together and stuck to the bottom of the kiln cause I'd used the fusing programme instead of annealling. Dohhhhh.
Sorry I had to laugh at that one Katie! Yes they seemed fine this morning - no cracks, passed the polarised filter test, (though I could only look at a fin of clear glass as the rest were opaque), but thank you everyone :)
Hmmm, thinking about it, if the strain point is 454 and my kiln seems to read quite a bit higher than room temperature in the mornings, then it could actually have been below the strain point, when showing 460...perhaps I will do a batch anneal on them to be on the safe side.
Marg - if you're planning another anneal as you go session - just pop the beads in before you turn the kiln on!
Looking forward to Friday!
Yeah, Trudi, I've started doing that (when I remember ::)) with little ones I've done in odd moments and left in the blanket ;D. Getting quite organised now, except when under pressure - then I do mad things like turn on the gas tank without closing the torch :-X
Roll on Friday! Lorna is coming too, according to another thread - be great to see her stringer magic close up!
Oh Marg, you and I would get along famously then, I've done the kiln thing many a time, and the gas cannister thing. ::) :P
And Katie - I've done the bead welding thing too - I cried - it was for a commission for a bracelet and I'd worked my socks off with limited time to complete it ....argh! :-*